Liquid composition

Chemical composition: Acrylate

Density: 1.08-1.12g/mL (tested under ASTM D792)

Viscosity: 220-300cps (tested under DHR-1 rheometer @ 25°C, 9.6s 1.25mm parallel plate rotor)

Color: transparent yellowish

Printable layer thickness: 0.05-0.2mm

Recommended bottom exposure: 40-60s

Recommended curing time: 5-16s

Cured composition

Hardness: 82-90 Shore D (tested under ASTM D2240)

Tensile Strength: 50-65MPa (tested under ASTM D638

Elastic modulus: 1500-2200 (tested under ASTM D638)

Elongation at break %: 10-25% (tested under ASTM D638)

Bending strength: 40-60MPa (tested under ASTM D790)

Flexural modulus: 1800-2300MPa (tested under ASTM D790)

Notched impact strength: 18-32 J/m (tested under ASTM D256)

Volume shrinkage %: 8.2 - 8.8% (tested under ASTM D792

Glass transition temperature: 65-100TG°C (tested under ASTM D7426-08)